doi:10.12034/j.issn.1009-606X.217348

过程工程学报 ›› 2018, Vol. 18 ›› Issue (3): 600-604.DOI: 10.12034/j.issn.1009-606X.217348

钒渣钙化焙烧熟料的浸出过程

罗富怀1,2，付念新1,2*，张林3，刘武汉3，涂赣峰1,2

1. 东北大学冶金学院，辽宁沈阳 110819；2. 东北大学多金属共生矿生态化利用教育部重点实验室，辽宁沈阳 110819; 3. 攀钢集团西昌钢钒有限公司，四川西昌 615012

收稿日期:2017-10-09 修回日期:2017-11-27 出版日期:2018-06-22 发布日期:2018-06-06
通讯作者: 付念新 funx@mail.neu.edu.cn

Leaching Process of Roasting Clinker with Vanadium Slag

Fuhuai LUO1,2, Nianxin FU1,2*, Lin ZHANG3, Wuhan LIU3, Ganfeng TU1,2

1. School of Metallurgy, Northeastern University, Shenyang, Liaoning 110819, China; 2. Key Laboratory of Ecological Utilization of Multimetallic Mineral, Ministry of Education, Northeastern University, Shenyang, Liaoning 110819, China; 3. Xichang Iron & Steel Co., Ltd., Pangang Group, Xichang, Sichuan 615012, China

Received:2017-10-09 Revised:2017-11-27 Online:2018-06-22 Published:2018-06-06
Contact: Nian-Xin FU funx@mail.neu.edu.cn

摘要/Abstract

摘要： The process of acid leaching of calcification roasted vanadium slag was studied. The effects of process parameters variation on phase of the vanadium leaching residue, leaching rate of vanadium and the reason of vanadium loss were analyzed. The results showed that the main phase of vanadium leaching residue was insoluble in acid of dense solid solution R2O3 and Fe2TiO5, which was also mixed with silicate pyroxene phase and small amount of vanadate phase. The vanadium leaching rate first increased and then decreased with raising the roasting temperature, roasting time and the CaO/V2O5 mass ratio. Silicate species and its effect on vanadate, spinel oxidation incomplete, vanadium and vanadium bronze solid solution in of R2O3, and the difference of best leaching acidity of Ca3V2O8, Ca2V2O7 and CaV2O6 were the causes of vanadium loss.

关键词: 钒渣, 钙化焙烧, 浸出率, 钒酸钙, 钒损失

Abstract: 对钒渣钙化焙烧后的熟料用硫酸浸出，分析了不同条件下焙烧的熟料对钒浸出渣物相、钒浸出率的影响及钒损失的原因. 结果表明，钒浸出渣的主要物相为不溶于酸的致密固溶体R2O3和铁板钛矿Fe2TiO5，其间混有硅酸盐辉石相和少量钒酸盐相. 钒浸出率随焙烧温度、焙烧时间和钙钒质量比增加呈先增加后减小的趋势. 硅酸盐种类及其对钒酸盐的影响、尖晶石氧化不完全、R2O3相中固溶V和钒青铜及正、焦、偏钒酸钙最佳浸出酸度不同是造成钒损失的原因.

Key words: vanadium slag, calcification roasting, leaching rate, calcium vanadate, vanadium loss

罗富怀付念新张林刘武汉涂赣峰 . 钒渣钙化焙烧熟料的浸出过程[J]. 过程工程学报, 2018, 18(3): 600-604.

Fuhuai LUO Nianxin FU Lin ZHANG Wuhan LIU Ganfeng TU. Leaching Process of Roasting Clinker with Vanadium Slag[J]. Chin. J. Process Eng., 2018, 18(3): 600-604.

参考文献

[1]付自碧，彭毅. 钒渣富氧钙化焙烧试验研究 [J]. 钢铁钒钛, 2014,35(4): 1-5. [2]Wang T Y, Xu L J. Calcified Roasting-Acid Leaching Process of Vanadium from Low-grade Vanadium-containing Stone Coal [J]. Chin. J. Geochem., 2014, 33(2): 163–167. [3]Bao S X, Liang L. Effect of Calcium on the Vanadium Extraction from High Calcium Type Stone Coal [J]. Journal of Wuhan University of Technology (Mater. Sci. Ed.), 2015, 30(2): 320-323. [4]包申旭，张一敏. 石煤焙烧过程中矿相与钒价态的变化及对钒浸出的影响 [J]. 矿冶工程, 2012, 32(2): 90-92. [5]Ognyanova A, Ozturk A T, De Michelis I, et al. Metal Extraction from Spent Sulfuric Acid Catalyst through Alkaline and Acidic Leaching [J]. Hydrometallurgy, 2009, 100(2): 20-28. [6]王永双. 用溶剂萃取法从炭质页岩中回收钒钼[J]. 稀有金属,1995(4):9-16 [7]赵博. 钒渣钙化焙烧机理的研究[D]. 东北大学,2014. [8]陈厚生. 钒渣石灰焙烧法提取V2O5工艺研究[J]. 钢铁钒钛,1992, 13(6): 1-9. [9]尹丹凤,彭毅,孙朝晖,何文艺. 攀钢钒渣钙化焙烧影响因素研究及过程热分析[J]. 金属矿山,2012,(04):91-94. [10]张菊花，张伟，杨勇霞. 钒渣钙化焙烧的影响因素及焙烧氧化动力学 [J]. 东北大学学报, 2014, 35(6): 831-835. [11]Zhang J H, Zhang W. Mechanism of Vanadium Slag Roasting with Calcium Oxide [J]. Int. J. Miner. Process., 2015, 138: 20-29. [12]Li X S, Xie B. Extraction of Vanadium from High Calcium Vanadium Slag Using Direct Roasting and Soda Leaching [J]. Int. J.Miner. Metall. Mater., 2012, 19(7): 595-601. [13]李晓军. 钒渣中尖晶石生长规律及钒渣钙化焙烧机理的研究[D]. 重庆大学,2011. [14]李新生. 高钙低品位钒渣焙烧-浸出反应过程机理研究 [D]. 重庆：重庆大学，2011: 66-69. [15]史志新，苑天宇. 钙化焙烧钒渣过程中钒尖晶石的矿物学特征[J]. 矿冶, 2014, 23(5): 95-98. [16]史志新，刘锦燕. 钒渣焙烧过程中物相的矿物学特征探讨 [J].冶金分析, 2014, 34(7): 12-17. [17]王春梅，刘锦燕，史志新，等. 钒渣物相结构及钙化焙烧相变对钒转化率的影响因素探讨 [J]. 冶金分析, 2015, 35(6): 26-30. [18]宋文臣，李宏，张勇健. X 射线光电子能谱分析钒渣熟料中钒的价态 [J]. 冶金分析, 2014, 34(4): 27-31. [19]付念新,张林,刘武汉,涂赣峰,隋智通. 钒渣添加石灰石氧化焙烧过程中物相的转化行为[J]. 过程工程学报,2017,17(02):285-291. [2017-09-13]. [20]田茂明. 含钒钢渣提钒工艺及其主要技术[J]. 重庆科技学院学报,2009,11（2）：59-63

钒渣钙化焙烧熟料的浸出过程

Leaching Process of Roasting Clinker with Vanadium Slag

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

[1]	王新东李兰杰杜浩赵备备. 亚熔盐高效提钒铬清洁生产技术产业化应用[J]. 过程工程学报, 2020, 20(6): 667-677.
[2]	隋智通娄太平霍守星. 弱氧化剂CO₂(g)对含钒铁水吹炼制钒渣的影响[J]. 过程工程学报, 2019, 19(S1): 45-50.
[3]	杨玮曹欢张凯王刚. 焙烧酸浸渣中铜的形态对铜、金浸出率的影响[J]. 过程工程学报, 2018, 18(6): 1226-1231.
[4]	张菊花严哲锋张力. 钙化提钒溶液沉钒的影响因素及沉钒动力学[J]. 过程工程学报, 2018, 18(1): 111-117.
[5]	耿立唐李兰杰赵备备白瑞国. 钒化工流程高效提取钒元素[J]. 过程工程学报, 2017, 17(4): 744-750.
[6]	付念新张林刘武汉涂赣峰隋智通. 钒渣添加石灰石氧化焙烧过程物相转化行为[J]. 过程工程学报, 2017, 17(2): 285-291.
[7]	阳亚玲颜文斌高峰. 离子交换树脂分离钒渣浸出液中钒与铬 [J]. 过程工程学报, 2017, 17(1): 84-91.
[8]	孟利鹏王少娜杜浩郑诗礼. 钒渣焙烧-碱浸提钒工艺焙烧过程机理[J]. 过程工程学报, 2016, 16(3): 445-451.
[9]	罗文波王吉坤赵兴凡王国卫张忠益. 含铟氧化锌烟尘加压硫酸浸出工艺优化[J]. 过程工程学报, 2015, 15(6): 982-987.
[10]	刘继鑫李兰杰郑诗礼王少娜杜浩谢海云. 钒渣焙烧-水热碱浸提钒[J]. , 2014, 14(5): 763-769.
[11]	范鹤林陈登福徐松龙木军龙海军. 高钙钒比钒渣钠化焙烧熟料浸出条件研究[J]. , 2013, 13(6): 958-963.
[12]	赵楚郑诗礼王少娜杜浩杨娜. 钒酸钾钙化沉钒法制备钒酸钙[J]. , 2013, 13(3): 442-446.
[13]	吕页清郑诗礼王少娜杜浩张懿. METSIM在亚熔盐法钒渣清洁生产工艺流程设计中的应用[J]. , 2013, 13(2): 270-274.
[14]	李晓军张润平谢兵. 钒渣钙化焙烧参数对钒浸出率的影响[J]. , 2012, 12(1): 54-58.
[15]	李兰杰张力郑诗礼娄太平张懿陈东辉陈东辉张燕. 钒钛磁铁矿钙化焙烧及其酸浸提钒[J]. , 2011, 11(4): 573-578.