钢渣改性活性炭的制备及其降解甲醛性能

张浩^1,2*，徐远迪¹，张磊¹，刘秀玉¹

1. 安徽工业大学建筑工程学院，安徽马鞍山 243032 2. 冶金减排与资源综合利用教育部重点实验室(安徽工业大学)，安徽马鞍山 243002

收稿日期:2019-02-10 修回日期:2019-03-31 出版日期:2019-12-22 发布日期:2019-12-22
通讯作者: 张浩 fengxu19821018@163.com
基金资助:
中国博士后科学基金资助项目;高校优秀青年骨干人才国外访学研修项目;安徽省博士后研究人员科研活动经费资助项目;安徽省级大学生创新创业训练计划项目;国家级大学生创新创业训练计划项目

Preparation of steel slag modified activated carbon and its formaldehyde degradation performance

Hao ZHANG^1,2*, Yuandi XU¹, Lei ZHANG¹, Xiuyu LIU¹

1. School of Civil Engineering and Architecture, Anhui University of Technology, Ma?anshan, Anhui 243032, China 2. Key Laboratory of Metallurgical Emission Reduction and Resources Recycling (Anhui University of Technology), Ministry of Education, Ma?anshan, Anhui 243002, China

Received:2019-02-10 Revised:2019-03-31 Online:2019-12-22 Published:2019-12-22
Contact: ZHANG Hao fengxu19821018@163.com

摘要/Abstract

摘要： 以钢渣和助磨剂(乙二醇、三乙醇胺和无水乙醇按体积比1:1:1混合)制备钢渣超细粉，用其对活性炭进行改性处理，获得钢渣改性活性炭，研究了钢渣种类、助磨剂用量和钢渣超细粉用量对钢渣改性活性炭降解甲醛性能的影响，分析了钢渣的化学成分、钢渣超细粉的粒度分布及结构、钢渣改性活性炭的微观结构。结果表明，450 g热闷渣与6 g助磨剂制备的钢渣超细粉用量10 g、活性炭30 g、无水乙醇50 g制备的钢渣改性活性炭具有良好的降解甲醛性能，12 h后甲醛降解率为60.9%。热闷渣中Fe2O3和MnO含量高，有利于甲醛在具有孔结构的活性炭中富集与催化降解；适量的助磨剂可显著减小钢渣超细粉的粒径，改善其粒度分布均匀程度，有利于增加钢渣超细粉与活性炭、甲醛的接触面积；可抵消由于活性炭孔隙率与比表面积降低导致的吸附性能下降，提高钢渣改性活性炭降解甲醛的性能。

关键词: 钢渣, 活性炭, 甲醛, 复合材料, 改性

Abstract: Steel slag ultrafine powder was prepared with steel slag and grinding aid, it was used to modify activated carbon to obtain steel slag modified activated carbon. The influences of types of steel slag, amount of grinding aid and amount of steel slag ultrafine powder on formaldehyde degradation performance of steel slag modified activated carbon were studied. Chemical composition of steel slag, particle size distribution and structure of steel slag ultrafine powder, and microstructure of steel slag modified activated carbon were characterized by XRF, LPSA, FT-IR, BET and SEM, respectively. The results showed that the steel slag modified activated carbon prepared under the conditions of steel slag was hot braised slag, amount of grinding aid (ethylene glycol, triethanolamine and absolute ethyl alcohol mixed with volume ratio 1:1:1) was 6 g, amount of steel slag ultrafine powder was 10 g, amount of activated carbon was 30 g and amount of absolute ethyl alcohol was 50 g had good formaldehyde degradation performance, degradation rate of formaldehyde after 12 h was 60.9%. The high contents of Fe2O3 and MnO in hot braised slag were conducive to formaldehyde enrichment and catalytic degradation in activated carbon with porous structure. Appropriate amount of grinding aid could significantly reduce the particle size and improve the particle size distribution uniformity of steel slag ultrafine powder, which was beneficial to increase the contact area of steel slag ultrafine powder, activated carbon and formaldehyde. Appropriate amount of steel slag ultrafine powder could offset activated carbon adsorption performance decline due to the decrease of porosity and specific surface area, improve the formaldehyde degradation performance of steel slag modified activated carbon.

Key words: steel slag, activated carbon, formaldehyde, composite material, modified

张浩徐远迪张磊刘秀玉. 钢渣改性活性炭的制备及其降解甲醛性能[J]. 过程工程学报, 2019, 19(6): 1228-1233.

Hao ZHANG Yuandi XU Lei ZHANG Xiuyu LIU. Preparation of steel slag modified activated carbon and its formaldehyde degradation performance[J]. Chin. J. Process Eng., 2019, 19(6): 1228-1233.

参考文献

[1] Chen L, Yin S F, Luo S L, et al. Bi2O2CO3/BiOI photocatalysts with heterojunctions highly efficient for visible-light treatment of dye-containing wastewater [J]. Ind. Eng. Chem. Res., 2012, 51(19): 6760?6768.
[2] Jing L Q, Xin B F, Yuan F L, et al. Effects of surface oxygen vacancies on photophysical and photochemical processes of Zn-doped TiO2 nanoparticles and their relationships [J]. J. Phys. Chem. B, 2006, 110(36): 17860?17865.
[3] Tojo S, Tachikawa T, Fujtsuka M, et al. Iodine-doped TiO2 photocatalysts: correlation between band structure and mechanism [J]. J. Phys. Chem. C, 2008, 112(38): 14948?14954.
[4] Zhao D, Peng T Y, Liu M, et al. Fabrication, characterization and photocatalytic activity of Gd3+-doped titania nanoparticles with mesostructure [J]. Microporous Mesoporous Mater., 2008, 114: 166?174.
[5] Hsu N Y, Chen P Y, Chang H W, et al. Changes in profiles of airborne fungi in flooded homes in southern Taiwan after Typhoon Morakot [J]. Science of the Total Environment, 2011, 409(9): 1677?1682
[6] 张浩，黄新杰，宗志芳，等. 基于吸附性能的生物质基多孔活性炭制备方案的响应面法优化[J]. 材料工程, 2017, 45(6): 67?72
Zhang H, Huang X J, Zong Z F, et al. Optimization of preparation program for biomass based porous active carbon by response surface methodology based on adsorptive property [J]. Journal of Materials Engineering, 2017, 45(6): 67?72
[7] 张浩. 基于傅里叶红外光谱的生物质环境协调功能材料制备机理及性能研究[J]. 光谱学与光谱分析, 2017, 37(2): 412?415
Zhang H. Study on preparation mechanism and property of biomass environmental coordination function material with fourier transform infrared spectrum [J]. Spectroscopy and Spectral Analysis, 2017, 37(2): 412?415
[8] Fang N J, Guo J X, Shu S, et al. Influence of textures, oxygen-containing functional groups and metal species on SO2, and NO removal over Ce-Mn/NAC [J]. Fuel, 2017, 202: 328?337
[9] Yao G H, Gui K T, Wang F. Low-temperature De-NOX by selective catalytic reduction based on iron-based catalysts [J]. Chemical Engineering & Technology, 2010, 33(7): 1093?1098
[10] Jie D, Qin Z, Zhang S. Catalytic efficiency of iron oxides in decomposition of H2O2, for simultaneous NOX, and SO2, removal: Effect of calcination temperature [J]. Journal of Molecular Catalysis A Chemical, 2014, 393(18): 222?231
[11] Kumar S, Kumar R, Bandopadhyay A, et al. Mechanical activation of granulated blast furnace slag and its effect on the properties and structure of portland slag cement [J]. Cement and Concrete Composites, 2008, 30(8): 679?685
[12] Ramezanianpour A A, Kazemian A, Moghaddam M A, et al. Studying effects of low-reactivity GGBFS on chloride resistance of conventional and high strength concretes [J]. Materials & Structures, 2016, 49(7): 2597?2609
[13] Morel F, Bounor-Legaré V, Espuche E, et al. Surface modification of calcium carbonate nanofillers by fluoro- and alkyl-alkoxysilane: Consequences on the morphology, thermal stability and gas barrier properties of polyvinylidene fluoride nanocomposites [J]. European Polymer Journal, 2012, 48(5): 919?929
[14] 张浩. 基于光催化性能的Cu-Ce/TiO2湿性能[J]. 材料工程, 2018, 46(1): 114?118
Zhang H. Cu-Ce/TiO2 moisture performance based on photocatalytic performance [J]. Journal of Materials Engineering, 2018, 46(1): 114?118
[15] Zhang H. Fang Y. Temperature dependent photoluminescence of surfactant assisted electrochemically synthesized ZnSe nanostructures [J]. Journal of Alloys and Compounds. 2019, 781: 201?208

钢渣改性活性炭的制备及其降解甲醛性能

Preparation of steel slag modified activated carbon and its formaldehyde degradation performance

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

[1]	王政德高凯雄张斌. 低温等离子体在电化学储能器件表面修饰的应用[J]. 过程工程学报, 2022, 22(9): 1159-1168.
[2]	赵晓腾周新涛罗中秋韦宇兰雄陆艳. 二氧化钛基复合材料对常见染料的去除性能及其机理研究进展[J]. 过程工程学报, 2022, 22(9): 1169-1180.
[3]	陶润萍董伟强胡庆松朱靖王智鑫徐轶群. Brij30/β-FeOOH/GO复合材料的可控构筑及其对盐酸四环素吸附性能[J]. 过程工程学报, 2022, 22(7): 979-988.
[4]	周育生邱冠周景建发郑富强王帅陈凤郭宇峰. 改性电炉钛渣矿相解构法制备富钛料新工艺研究[J]. 过程工程学报, 2022, 22(5): 651-659.
[5]	肖邦曹青马培勇毕海林李鹏程. 基于分子动力学模拟的羟基改性调控活性炭对甲苯吸附性能的作用机理研究[J]. 过程工程学报, 2022, 22(5): 660-670.
[6]	张凯伦焦念明张莹郝鹏波张国霞王慧李增喜. 双金属改性ZSM-5-USY复合分子筛催化裂解正己烷制备低碳烯烃[J]. 过程工程学报, 2022, 22(4): 458-468.
[7]	李燕郭昌进丁磊. 磁性离子交换树脂强化水源中有机物去除性能研究[J]. 过程工程学报, 2022, 22(4): 542-551.
[8]	李明哲马淑花王建兵王晓辉姚同宇刘晨旭. 改性粉煤灰对沙土物理特性改良效果研究[J]. 过程工程学报, 2022, 22(2): 204-213.
[9]	梁锐李明阳高翔鹏于先坤童雄龙红明. 选矿废水中残留黄药光催化处理及降解效率改进方式研究进展[J]. 过程工程学报, 2022, 22(1): 1-13.
[10]	张智霖, 丁磊, 周强, 余剑, 郭昌进, 张德伟. 响应曲面法优化木薯酒精污泥基活性炭制备及对没食子酸的吸附性能[J]. 过程工程学报, 2021, 21(7): 794-806.
[11]	马越周新涛黄静罗中秋符义忠母维宏王路星邵周军. 矿物掺合料对磷酸镁水泥性能影响及机理研究现状[J]. 过程工程学报, 2021, 21(6): 629-638.
[12]	王大鹏范宝安郭芬胡雅. 活性炭表面改性对其比电容及储能机理的影响[J]. 过程工程学报, 2021, 21(6): 724-733.
[13]	韩云龙纪杰杨小白钱付平胡永梅. 烧结烟气活性炭脱硝机制[J]. 过程工程学报, 2021, 21(5): 495-505.
[14]	王燕黄云姚华徐祥贵黄巧王君雷马普生王军生. 太阳盐/钢渣定型复合相变储热材料的制备与性能研究[J]. 过程工程学报, 2021, 21(3): 332-340.
[15]	董晓晗盛轲焱陈志炎黄江顾彦龙. 纤维素辐照改性及其应用[J]. 过程工程学报, 2021, 21(12): 1395-1402.